up to 10 times the nominal product size or 150 mm, whichever is shorter, shall be cold headed, except that they may be hot headed by special agreement of the purchaser. Larger sizes and longer lengths may be cold or hot headed at option of the manufacturer.
4.8、5.8、8.8、9.8和10.9级螺栓、螺钉，尺寸≤M20、长度是小于等于产品公称尺寸10倍或≤150mm须冷镦成型，客户特别要求热锻成型的除外。大尺寸或较长尺寸的产品则可由制造者自行决定使用冷锻或热锻成型。
4.3 Threading Practice — Class 4.8, 5.8, 8.8, 9.8, and 10.9 bolts and screws in sizes up to M20 inclusive, and lengths up to 150 mm inclusive, shall be roll threaded, except by special agreement. Threads of all sizes of class 4.6 bolts and screws and class 4.8, 5.8, 8.8, 9.8, and 10.9 bolts and screws in sizes over M20 and/or lengths longer than 150 mm, may be rolled, cut, or ground, at option of the manufacturer. Threads of all classes and sizes of studs may be rolled, cut, or ground at option of the manufacturer.
螺纹成型 – 4.8、5.8、8.8、9.8和10.9级螺栓、螺钉，尺寸≤M20，长度≤150mm, l螺纹须滚制成型，客户特殊要求除外。4.6级螺栓、螺钉所有尺寸的螺纹，4.8、5.8、8.8、9.8和10.9级的螺栓、螺钉的螺纹，尺寸＞M20 级及/或长度＞150mm,可采用滚制、切削或磨削方式进行制造，由制造商自行决定。所有等级及所有尺寸的螺柱的螺纹可采用滚制、切削或磨削方式进行制造，由制造商自行决定。
4.4 Heat Treatment Practice 热处理
4.4.1 Class 4.6 bolts and screws and class 4.6, 4.8, and 5.8 studs need not be heat treated. Class 4.8 and 5.8 bolts and screws shall be stress relieved if necessary to assure the soundness of the head to shank junction. When specified by the purchaser, class 5.8 bolts and screws shall be stress relieved at a minimum stress relief temperature of 470 °C. Where higher temperatures are necessary to relieve stresses in severely upset heads, mechanical requirements shall be agreed upon by manufacturer and purchaser.
等级4.6的螺栓、螺钉以及等级4.6、4.8和5.8级的螺柱不需要热处理。4.8和5.8级的螺栓、螺钉如必要的话须消除应力，以保证头杆连接处的稳固性。如买方特别指定，5.8 级螺栓、螺钉应在最小 470℃温度下消除应力。当需要更高的温度来消除应力时，机械性能要求须买卖双方达成一致。
4.4.2 Class 8.8 and 9.8 bolts, screws, and studs shall be heat treated, quenched in oil or water-base quenchant at the option of the manufacturer, and tempered at a minimum tempering temperature of 425 °C for class 8.8 and 410 °C for class 9.8. For class 9.8 screw and washer assemblies (sems), quenchants whose principal constituent is water shall NOT be used, and tempering temperature shall be no less than 340 °C. See also 4.4.5.
8.8和9.8级螺栓、螺钉及螺柱应进行热处理，油淬或水淬供应商自行决定，8.8级最小回火温度425℃、9.8级最小回火温度410℃。对于9.8级螺钉与垫片组件不得使用主要成分为水的淬火介质，回火温度不得低于340℃。亦可见4.4.5。
4.4.3 Medium carbon alloy steel class 10.9 bolts, screws, and studs shall be heat treated, oil quenched, and tempered at a minimum tempering temperature of 425 °C. Low-carbon martensite steel class 10.9 bolts, screws, and studs shall be heat treated, quenched in oil or water-base quenchant at the option of the manufacturer, and tempered at a minimum tempering temperature of 340 °C. See also 4.4.5.
10.9级中碳合金钢螺栓、螺钉应进行热处理，淬火介质油，最小回火温度425℃。10.9级低碳马氏体钢螺栓、螺钉和螺柱应进行热处理，油淬或水淬制造商自行决定，回火温度不得
低于340℃。亦可见4.4.5。
4.4.4 Under no circumstances should heat treatment or carbon restoration be accomplished in the presence of nitrogen compounds, such as carbonitriding or cyaniding.
在任何情况下的热处理或碳恢复须在氮化合物存在下完成，如碳氮共渗或 氰化处理。
4.4.5 Tempering Temperature Audit Test (for checking whether products have been tempered at specified temperature). Conduct hardness test (ASTM F 606M) on one or more bolts, screws, or studs; retemper the product(s) at a temperature 10 °C less than the specified minimum tempering temperature for 30 min; repeat product hardness test. The difference between the mean hardnesses (before and after retempering) shall be no greater than 2 points Rockwell C (approximately 20 Vicker points).
回火温度监视测试（检查产品是否按技术规定的温度进行回火）。在一个或多个螺栓、螺钉或螺柱上进行硬度测试（依据标准ASTM F 606M）；重回火产品回火温度低于最小规范温度10℃；然后对回火产品进行硬度测试。平均硬度之间的差异（重回火前后的硬度）不得超过两个HRC 硬度点（大约20个维氏硬度点）。
5 Mechanical and Physical Properties 力学与物理性能
5.1 Mechanical — Bolts, screws, and studs shall be tested in accordance with the mechanical testing requirements for the applicable type, property class, size, and length of product as specified in Tables 3A and 3B, and shall meet the mechanical requirements specified for that product in Tables 1A and 1B.
力学性能- 螺栓、螺钉和螺柱应按表3A和3B规定的机械性能测试要求对相应类型、等级、公称尺寸和长度进行测试，并满足表1A和1B规定的产品机械性能要求。
5.2 Decarburization—Unless otherwise specified, class 8.8 and 9.8 products shall conform to decarburization class 1/2H and Class 10.9 products shall conform to decarburization class 2/3H as specified in SAE J121M.
脱碳- 除非另有规定，8.8和9.8级产品脱碳等级应符合SAE J121M规定的1/2H级，10.9级产品脱碳等级应符合2/3H级要求。
5.3 Surface Discontinuities 表面不连续性
5.3.1 Bolts, screws, and studs of classes 8.8, 9.8, and 10.9 in sizes up to M24 inclusive, and lengths up to 150 mm inclusive, shall not have surface discontinuities exceeding the limits specified in SAE J1061.
8.8、9.8、和10.9级的螺栓、螺钉和螺柱，尺寸≤M24，长度≤150mm，表面不连续性不得超过SAE J1061 规定的限制。
Surface discontinuities for sizes and lengths of products not covered in the scope of SAE J1061 shall be within limits specified by purchaser.
对于没有含括在SAE J1061中的尺寸和长度的产品的表面不连续性限制应满足买方指定的要求。
5.3.2 When the engineering requirements of the application necessitate that surface discontinuities must be more closely controlled, the purchaser shall specify the applicable limits in the original inquiry and purchase order. For certain fasteners, this may be done by reference to SAE J123. 当适用需要工程要求表面不连续性控制加严时，买方需在最初询盘和采购订单中规定适用限制。对某些紧固件，SAE J 123 可作参考。
6 Methods of Test 测试方法
6.1 General—Procedures for conducting the tests to determine the mechanical properties as
specified in Tables 3A and 3B for the applicable product, property class, size, and length are given in ASTM F 606M. Tables 3A and 3B specifies the applicable test method to be followed when determining each mechanical property.
通用方法-依据ASTM F 606M 规程进行测试以确定相应产品、等级、尺寸和长度是否符合表3A和3B中规定的性能等级。表3A和3B规定了适用的测试方法以确定每一机械性能。 表3A-螺栓、螺钉和螺柱机械性能测试要求 规定的最小性能产品 短螺栓螺钉 特殊头部螺栓螺钉（5） 产品硬度最大产品长度（1） （2） 全尺寸产产品硬度最小（2） 全尺寸产品楔形抗拉强度测试（2）（4）全尺寸产品轴向抗拉强度测试（2）产品抗拉强度kN 所有 所有 表面硬度（2）（3） 品保证载荷测试(2) 等级 所有 所有 小于2-1/4D 所有 2-1/4D至8D. . . . . - . . . - - 。 - - . - - - 所有 450及以下 或200mm, 视何者较长而定 超过8D或六角头螺栓螺钉（6）（7） 所有 450及以下 200mm, 视何者较长，到300mm(含) . . . . . . . - - - - - - . . . . . . . . 。 . 。 。 。 。 - . A A - - - - - - - . A A - 所有 450及以下 超过300mm 2-1/4D及以上 2-1/4D至8D所有 大于450 所有 其他螺栓螺钉 所有 450及以下 或200mm, 视何者较长 超过8D或450及以下 200mm, 视何者较长 所有 短螺柱 所有 大于450 所有 2-1/4D及以上 小于2-1/4D 2-1/4D至8D其它螺柱 所有 450及以下 或200mm, 视何者较长 . - . 。 . - 超过8D或其它螺柱 所有 450及以下 200mm, 视何者较长 . . 3.1 - - 3.1 . . 3.1 。 。 3.2 A A 3.5 - - 3.4 所有 测试依据ASTM F 606M章节 大于450 2-1/4D及以上 1、 D等于产品公称尺寸。为表 3 的要求：“产品长度”为一般长度包含尾端倒角如 ASME B18.2.1 所定义， 其他特殊尾端产品必须从承面到完整牙型的端部。 2、“.”是强制试验标识。每一产品所有强制试验项目都必须进行。另外所有测试选项的指示， A标识测试（全尺寸产品）和B标识测试（加工试验件）都要进行测试；B测试项不适用于尺寸≤M24。“。”项当最初询盘和订单有规定时，须进行测试。有争议时，“A”和“。”项都要进行测试。破折号（-）代表不需要进行测试。 3、表面硬度及脱碳要求仅适用于8.8、9.8、10.9级产品。 4、抗拉强度楔形角度见表4. 5、异形螺栓、螺钉是指特殊结构或者头部有钻孔的产品，其头部强度比螺纹段脆弱。 6、包括法兰、垫片及其他六角头造形的产品，其强度不比螺纹段弱。 7、包括9.8级组件以及像组件一样加工的9.8级无垫片产品（尺寸1.6≤M≤12）。为了确定拉伸试验的适用性，组件长度测量从不平垫片的支撑面的底面到螺钉全螺纹螺杆末端。 表3B-螺栓、螺钉和螺柱机械性能测试要求 规定的最小性能产品 短螺栓螺钉 特殊头部螺栓螺钉（4） 加工试样件屈服强度测产品长度（1） 加工试样件抗拉强度测试（2） 产品抗拉强度kN 所有 所有 加工试样件伸长率（2） 加工试样件端面收缩率（2） 等级 所有 所有 试（2） 螺纹段脱碳2（）（3） 小于2-1/4D 所有 2-1/4D至8D- - - - - - - - - - - - 。 。 。 所有 450及以下 或200mm, 视何者较长为准 超过8D或六角头螺栓螺钉（5）6） 所有 450及以下 200mm, 视何者较长为准，到300mm(含) - B B - B B - B B - B B 。 所有 450及以下 超过300mm 2-1/4D及以上 2-1/4D至8D。 。 。 所有 大于450 其他螺栓螺钉 所有 450及以下 或200mm, 视何者较长为准 - - - - 超过8D或所有 450及以下 200mm, 视何者较长为准 B B B B B B B B 。 。 。 。 所有 大于450 2-1/4D及以上 短螺柱 所有 所有 小于2-1/4D 2-1/4D至8D- - B B ASTM F 606M 3.6 - - B B ASTM F 606M 3.6 - - B B ASTM F 606M 3.6 - - B B ASTM F 606M 3.6 所有 450及以下 或200mm, 视何者较长 其它螺柱 超过8D或所有 450及以下 200mm, 视何者较长为准 。 。 SAE J121M 所有 大于450 2-1/4D及以上 测试依据章节 1、 D等于产品公称尺寸。为表 3 的要求：“产品长度”为一般长度包含尾端倒角如 ASME B18.2.1 所定义， 其他特殊尾端产品必须从承面到完整牙型的端部。 2、“.”是强制试验标识。每一产品所有强制试验项目都必须进行。另外所有测试选项的指示， A标识测试（全尺寸产品）和B标识测试（加工试验件）都要进行测试；B测试项不适用于尺寸≤M24。“。”项当最初询盘和订单有规定时，须进行测试。有争议时，“A”和“。”项都要进行测试。破折号（-）代表不需要进行测试。 3、表面硬度及脱碳要求仅适用于8.8、9.8、10.9级产品。 4、特殊头部螺栓、螺钉是指特殊结构或者头部有钻孔的产品，其头部强度比螺纹段脆弱。 5、包括法兰、垫片及其他六角头造形的产品，其强度不比螺纹段弱。 6、包括9.8级组件以及像组件一样加工的9.8级无垫片产品（尺寸1.6≤M≤12）。为了确定拉伸试验的适用性，组件长度测量从不平垫片的支撑面的底面到螺钉全螺纹螺杆末端。 表4-抗拉测试楔形角度 产品 六角头、华司头机加螺钉 六角螺栓、螺钉螺纹1D并接近头部底部 六角法兰、司华头机加螺栓、螺钉 其他六角螺栓、螺钉 螺柱 性能等级 4.8、9.8 8.8、9.8、10.9 4.6、4.8、5.8、8.8、9.8、10.9 4.6、4.8、5.8、8.8、9.8、10.9 所有 公称尺寸 M10及以下 M20及以下 M20＜M≤M36 M36及以下 M24及以下 M24＜M≤M36 M20及以下 M20＜M≤M36 楔形角度 6 6 4 6 10 6 6 4