| 0.51 | 74.87 | 107.09 | 5.94 | 22.12 | V | | 0.54 | 79.71 | 109.24 | 6.70 | 22.12 | V | | 0.57 | 84.38 | 112.28 | 7.62 | 22.13 | V | | 0.60 | 89.03 | 116.43 | 8.78 | 22.17 | V | | 0.63 | 93.69 | 120.69 | 10.17 | 22.17 | V | | 0.65 | 96.35 | | | | V/P | | 0.66 | 97.37 | 98.83 | 10.64 | 9.62 | P | | 0.69 | 98.57 | 98.83 | 12.64 | 5.63 | P | | 0.72 | 99.35 | 98.83 | 13.26 | 3.97 | P | | 0.74 | 99.75 | 98.83 | 13.66 | 3.14 | P | | 0.75 |100.00 | 98.83 | 13.94 | 2.85 |Filled |
|--------------------------------------------------------------------------------------| Execution time in Filling Phase = 318.11 s
保压分析过程信息：
Packing phase:
|-------------------------------------------------------------------------------------| | Time |Packing| Pressure | Clamp force| Status | | (s) | (%) | (MPa) | (tonne) | | |-------------------------------------------------------------|
| 0.75 | 0.00 | 98.83 | 13.95 | P | | 0.80 | 0.65 | 98.83 | 16.70 | P | | 1.41 | 8.35 | 98.83 | 10.31 | P | | 1.66 | 11.52 | 98.83 | 6.13 | P | | 2.16 | 17.85 | 98.83 | 3.03 | P | | 2.41 | 21.01 | 98.83 | 2.44 | P | | 2.85 | 26.62 | 78.61 | 1.74 | P | | 3.31 | 32.38 | 33.66 | 1.18 | P | | 3.56 | 35.55 | 8.95 | 0.93 | P | | 3.81 | 38.71 | 0.00 | 0.75 | P | | 3.81 | | | |Pressure released| |-----------------------------------------------------------------------------------| | 4.06 | 41.88 | 0.00 | 0.63 | P | | 4.56 | 48.21 | 0.00 | 0.47 | P | | 4.81 | 51.37 | 0.00 | 0.41 | P | | 5.31 | 57.70 | 0.00 | 0.31 | P | | 5.56 | 60.87 | 0.00 | 0.27 | P | | 6.06 | 67.20 | 0.00 | 0.20 | P | | 6.56 | 73.53 | 0.00 | 0.15 | P | | 6.81 | 76.70 | 0.00 | 0.13 | P | | 7.31 | 83.03 | 0.00 | 0.12 | P | | 7.56 | 86.19 | 0.00 | 0.11 | P | | 8.06 | 92.52 | 0.00 | 0.10 | P | | 8.31 | 95.69 | 0.00 | 0.09 | P |
第 26 页 共 30 页
| 8.81 |100.00 | 0.00 | 0.09 | P |
-------------------------------------------------------------------------------------
（三）结果分析（配合截图说明） （1）填充时间：
（2）熔接痕;
第 27 页 共 30 页
(3)转换点压力：第 28 页 共 30 页
（3）XY Plot浇口位置压力曲线：
第 29 页 共 30 页
（4）翘曲分析;
总体最大变形量：0.4957mm X方向最大变形量：0.2218mm
Y方向最大变形量：0.4791mm Z方向最大变形量：0.0850mm （四）小结：
通过对手机面板实例的分析，进行了最佳浇口位置分析，利用最佳位置的分析结果，给出了初步设计方案及相应成型模拟过程，通过计算结果的分析，发现了成型熔接痕存在较大的缺陷，经过对初步设计方案的调整，基本解决了这一问题，找到了最佳的浇口位置。